From the polarization
curve, it can be seen that there is a shift in the ECORR towards
the positive direction for the Cu+G sample. It proves the
graphene coating acts as a corrosion resistance barrier.
Meanwhile, the current densities enable the oxygen reduction
reaction rate to be determined.